| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 熔體流動(dòng)速率 | ASTM D-1238 | 4.5 | g/10min. | |
| 機(jī)械性能 | 彎曲強(qiáng)度 | ASTM D-790 | 900(88) | kg/cm2(MPa) | |
| Izod沖擊強(qiáng)度 | ASTM D-256 | 1.9(19) | kg-cm/cm(J/m) | ||
| 抗張強(qiáng)度 | ASTM D-638 | 450(44) | kg/cm2(MPa) | ||
| 彎曲模數(shù) | ASTM D-790 | 3.4(3330) | kg/cm20000(MPa) | ||
| 伸長(zhǎng)率 | ASTM D-638 | 2.2 | % | ||
| 抗張模數(shù) | ASTM D-638 | 1.8(1770) | kg/cm20000(MPa) | ||
| 熱性能 | 衛(wèi)氏軟化點(diǎn) | ASTM D-648 | 95 | ℃ | |
| 熱變形溫度 | ASTM D-648 | 91 | ℃ | ||
| 衛(wèi)氏軟化點(diǎn) | ASTM D-1525 | 95 | ℃ | ||
| 熱變形溫度 | ASTM D-1525 | 91 | ℃ | ||
| 其它性能 | 殘留單體 | 700 | ppm max | ||
| 燃燒性 | 1/16" | HBNC | UL-94FILE NO.E117170 | ||